Pechini method was used in order to obtain fine ceramic and single-phase powders for a lead-free ferroelectric system 0,97[(Bi_1/2Na_1/2)_1-x(Bi_1/2K_1/2)xTiO₃]-0,03[(Na_1/2K_1/2)NbO₃]or BNKT-KNN (x = 0.00, 0.18, 0.21, 0.24, 0.27). This method allowed obtaining powders with 100 % perovskite phase, which was confirmed by X-ray diffraction, for this particular system in all the studied stoichiometries using temperature as low as 600 ºC. The effects on the bonds present in the structure due to variation of the stoichiometry, Na-K, were determined using infrared spectroscopy, FT-IR. Irregular nanoparticles were observed by scanning electron microscopy.

El método Pechini fue utilizado para obtener polvos cerámicos finos y monofásicos del sistema ferroeléctrico libre de plomo 0,97[(Bi_1/2Na_1/2)_1-x(Bi_1/2K_1/2)xTiO₃]-0,03[(Na_1/2K_1/2)NbO₃] ó BNKT-KNN (x = 0.00, 0.18, 0.21, 0.24, 0.27). Este método permitió la obtención de polvos con 100 % de fase perovskita, para el sistema de interés en todas las estequiometrias estudiadas, a una temperatura tan baja como 600 ºC, lo que fue confirmado por difracción de rayos X. Por medio de espectroscopia infrarroja, FT-IR, se pudo determinar cómo afecta la variación de la estequiometria, Na-K, los enlaces presentes en la estructura. Mediante microscopia electrónica de barrido se observaron partículas nanométricas irregulares.