In this study, SnO2 semiconductor nanoparticles were synthesized for DSC applications via acid route using tin(ii) chloride as a starting material and hydrothermal method through the use of tin(iv) chloride. Powder X-ray diffraction studies confirmed the formation of the rutile phase of SnO2 with nanoranged particle sizes. A quasi-solid-state electrolyte was employed instead of a conventional liquid electrolyte in order to overcome the practical limitations such as electrolyte leakage, solvent evaporation, and sealing imperfections associated with liquid electrolytes. The gel electrolytes were prepared incorporating lithium iodide (LiI) and tetrapropylammonium iodide (Pr4N+I−) salts, separately, into the mixture which contains polyacrylonitrile as a polymer, propylene carbonate and ethylene carbonate as plasticizers, iodide/triiodide as the redox couple, acetonitrile as the solvent, and 4-tertiary butylpyridine as an electrolyte additive. In order to overcome the recombination problem associated with the SnO2 due to its higher electron mobility, ultrathin layer of CaCO3 coating was used to cover the surface recombination sites of SnO2 nanoparticles. Maximum energy conversion efficiency of 5.04% is obtained for the device containing gel electrolyte incorporating LiI as the salt. For the same gel electrolyte, the ionic conductivity and the diffusion coefficient of the triiodide ions are 4.70 × 10−3 S cm−1 and 4.31 × 10−7 cm2 s−1, respectively.