The porcelain stoneware tiles production needs high whiteness´ clays in order to be competitive in the ceramic sector. In the present work, Spanish clays used in the porcelain stoneware tiles production have been characterized in physic, chemist and mineralogical terms, in order to reduce its content of chromophore oxides (Fe₂O₃ and TiO₂). These reduction processes are concerned with different physical and chemical treatments, as sieving at 150μm, magnetic separation using a 0.6T permanent magnet, or acid treatment with HCL and later neutralization with NH₃. With these treatments, due to siderite elimination, chromophore oxides as Fe₂O₃ have been decreased from 2,36% to 1,66% in the chemically treated clay.<br><br>En el proceso de fabricación de baldosas de gres porcelánico es necesario utilizar arcillas con un elevado grado de blancura, debido sobre todo a las exigencias del mercado. En el presente trabajo, se ha caracterizado física, química y mineralógicamente una arcilla nacional utilizada en el sector de fabricación de baldosas de gres porcelánico español, para posteriormente y, con el objetivo de reducir su contenido en óxidos cromóforos (Fe₂O₃, TiO₂), someterla a diversas etapas físico-químicas, como son el tamizado a 150 μm de luz de malla, la separación magnética mediante un imán permanente de 0.6T, el ataque ácido con HCl y posterior neutralización con NH₃. Con estas técnicas, se ha podido reducir el contenido en Fe₂O₃, debido principalmente a la eliminación de siderita, pasando de un 2,36% inicial hasta un 1,66% en la arcilla tratada químicamente.