Phase, Composition and Structure Changes of CoCrNi-Based Concentrated Alloys Resulting from High Temperature Oxidation
Abstract
In this work, CoCrNi, FeCoCrNi and CoCrFeMnNi concentrated alloys with a Y-Ti oxide particle dispersion were prepared by mechanical alloying and Spark Plasma Sintering. The alloy consists of an FCC Ni-based matrix with a Y-Ti oxide dispersion and additional phases of Cr23C6 and Cr2O3. The effect of Fe, Mn, and Y-Ti oxide particles on the formation of oxide scales and the composition of the adjacent CoCrNi and FeCoCrNi alloys was studied. It was found that alloys without Mn in their composition form a protective Cr2O3 scale. The Cr23C6 particles provide an alternative mechanism for balancing the chromium loss during the oxidation. Y and Ti from the oxide particles participate in the formation of the protective oxide scales. Fe promotes Y and especially Ti diffusion through the Cr2O3 scale, resulting in the formation of Ti-depleted regions in the alloy. The findings will serve for the further development of these new materials.
Keywords
Access
Citation
ID:
110747
References
Blockchain Verification
Account:
NFT Contract Address:
0x95644003c57E6F55A65596E3D9Eac6813e3566dA
Article ID:
110747
Unique Identifier:
10.3390/ma13102276
Network:
Scimatic Chain (ID: 481)
Loading...
Blockchain Readiness Checklist
Authors
Abstract
Journal Name
Year
Title
Creates 1,000,000 NFT tokens for this article
Token Features:
- ERC-1155 Standard NFT
- 1 Million Supply per Article
- Transferable via MetaMask
- Permanent Blockchain Record
Scan with Saymatik Web3.0 Wallet