The thin-walled airfoil areas of as-cast single-crystalline turbine blades made of CMSX-4 superalloy were studied. The blades were produced by the industrial Bridgman technique at withdrawal rates of 2, 3 and 4 mm/min. The angle between the [001] crystallographic direction and blade axis, related to the primary orientation, was defined by the Ω-scan X-ray diffraction method at points on the camber line located near the tip of an airfoil and at points of a line located in parallel and near the trailing edge. Additionally, primary crystal orientation was determined by Laue diffraction at the selected points of an airfoil. The influence of mould wall inclination on the primary crystal orientation of the thin-walled areas is discussed. The effect of change in the [001] crystallographic direction, named as "force directing", was considered with regard to the arrangement of primary dendrite arms in relation to the trailing edge and the camber line. It was stated that when the distance between the mould walls is less than the critical value of about 1.5 mm the "force directing" increases as the distance between the walls of the mould decreases. The effect may be controlled by selecting an appropriate secondary orientation using a seed crystal in the blade production process. The model of dendrite interaction with the mould walls, including bending and "deflection", was proposed.