The aim of this paper is to introduce HSBM as a green and environmentally friendly technique for the synthesis of thiochromeno[4,3-b]pyran and benzo[h]thiazolo[2,3-b]quinazoline derivatives over ZnAl2O4 nanopowders as an efficient catalyst.ZnAl2O4 nanopowders were synthesized via a co-precipitation of Zn(NO3)2 and Al(NO3)3 salts and were characterized by XRD, FE-SEM, TEM and DLS techniques. The as-prepared ZnAl2O4 nano-powders have been used as catalyst on the synthesis of pyran nucleus using high-speed ball milling (HSBM) technique. The structure of products was confirmed with NMR analysis.ZnAl2O4 exhibit a cubic crystal structure (Space group: Fd-3m) with the average crystallite size of 41 nm. The average particle size of ZnAl2O4 nano-powders determined by DLS technique is 55 nm. The catalytic activity of nano-powders was examined on the synthesis of 2-amino-4,5-dihydro-4-arylthiochromeno[4,3-b]pyran-3-carbonitriles, (8Z)-2-amino-8-arylidene-4,5,7,8-tetrahydro-4-arylthiopyrano[4,3-b]pyran-3-carbonitriles, 4-aryl-3,4,5,6-tetrahydrobenzo[h]quinazoline-2(1H)-thiones and 4-aryl-1,3,4,5-tetrahydro-2H-thiochromeno[4,3-d]pyrimidine-2-thione derivatives. All products were obtained in high yields with short reaction times.ZnAl2O4 nanopowders were prepared via a cost-effective co-precipitation method and showed a good potential for the synthesis of 4H-pyran analogous in good yields. The salient advantages of HSBM technique include environmentally friendly as it was reduced solvents, is a simple technique and has low energy costs.